It is shown that a regular pattern distribution of scattered alloying zones which surrounded by phase transformation zone can retard the fatigue crack growth rate and improve the fatigue life.
研究表明,大量规则分布、互不重叠的合金化区及其周围的相变硬化区从总体上降低了疲劳裂纹扩展速率,提高了材料的疲劳寿命。
Fracture mechanics is adopted to estimate the fatigue life of structural members, and among the rest, crack growth rate formula is studied.
本文采用断裂力学方法来估算结构构件的疲劳寿命,这其中主要围绕裂纹扩展速率表达式展开研究。
The fatigue crack growth rate is the core for predicting fatigue life by use of fatigue crack propagation (FCP) theory.
疲劳裂纹扩展率表达式是采用疲劳裂纹扩展理论预报疲劳寿命的核心。