The large welding current caused the formation of quenched martensite and the high residual stresses in the welding zone, resulting in the increase of zinc sensitivity of hydrogen attack.
结果表明:由于焊接电流过大,使焊缝产生淬火马氏体组织及较大的焊接残余应力,导致镀锌氢脆敏感性增加,造成吸油盘发生氢脆开裂。
The results indicate that with the increase of the welding current, welding press and electrifying time, there are decreased in rate of false welding and increased in pressed depth.
结果表明:当焊接电流越强,电极压力越大,焊接通电时间越长时,钢筋网焊点虚焊率越低,压入深度越大。
Welding current can be set to increase compensation.
可设定焊接电流递增补偿。