This paper advanced a study method that can observe plastic deformation behavior of surface layer of die cavity by showing austenite grain, size, crack morphology and propagation mode.
提出了通过显示奥氏体实际晶粒度、裂纹形貌和扩展方式来分析热锻模具型腔表层塑性变形行为的试验方法。
The oxidation degree of grain boundaries and crack propagation are qualitatively analyzed based on crack density and percentage of intergranular crack.
用裂纹密度和晶界裂纹的比例对晶界氧化的程度及裂纹扩展情况定性地加以分析。
Tranagranular cracks result from deformation damage of grain, and its propagation mechanism is shear rupture along slip plane.
穿晶裂纹源于晶内形变损伤区，其扩展机制为沿滑移面的剪切断裂。