According to analysis result of tubes' cracks fracture observation, it proves that the fracture is quasi-cleavage fracture which is characterized by river pattern.
通过对管束大量电子断口的观察分析，证明了断口为准解理断裂，具有河流花样的特征。
The cracks on blades made of a directionally solidified superalloy were analyzed. The failure mode and cause were studied in virtue of fracture observation and metallographic analysis.
对定向凝固合金叶片的裂纹进行分析，在断口观察与金相组织分析的基础上，对叶片的失效模式与失效原因进行研究，并提出预防该类故障发生的措施。
The fracture of blades made of a directionally solidified superalloy was analyzed. The failure mode and cause were studied in virtue of fracture observation and metallographic structure analysis.
对定向凝固合金叶片的断裂故障进行了分析，在断口观察与金相组织分析的基础上，对叶片的失效模式与失效原因进行了研究，并提出了预防该类故障发生的措施。