Quenching crack propagation characteristics of the organizations on both sides without decarburization phenomenon significant difference between crack and materials and forging cracks.
淬火裂纹的组织特征是裂纹两侧无脱碳现象，明显区别与锻造裂纹和材料裂纹。
Causes the steel to produce the hot brittleness, reduces the steel the ductility and the toughness, when forging and rolling crack.
使钢产生热脆性，降低钢的延展性和韧性，在锻造和轧制时形成裂纹。
Improper forging process will also appear large grain or uneven, hardening crack phenomenon, forging cost is higher than the casting flange.
锻造工艺不当也会出现晶粒大或不均，硬化裂纹现象，锻造成本高于铸造法兰。