The Ferrite Rolling 铁素体轧制
ferrite rolling technology 铁素体轧制工艺
ferrite region rolling 铁素体区轧制
ferrite range rolling 铁素体区轧制
rolling in ferrite area 铁素体轧制
rolling in ferrite region 铁素体区轧制
rolling in ferrite domains 铁素体区轧制
The results showed that the if steel has better deep drawability, higher mechanical and texture strength and elongation if the hot rolling temperature was low with big reduction in ferrite region.
结果表明,较低的铁素体轧制温度和较高的铁素体区压下量时,IF钢具有更高的深冲性能、相对较高的强度、延伸率以及织构强度。
According to the above mathematical model, it can calculate final ferrite grain size after rolling cooling.
按照上述给出的数学模型,可计算出轧制冷却后最终的铁素体晶粒的大小。
The results show that polygonal ferrite, granular bainite and larger amount of stabilized retained austenite can be obtained after hot rolling.
结果表明,热轧后能够获得多边形铁素体、粒状贝氏体和大量稳定的残留奥氏体组织。