FLASH : Green roller defect, caused by excessive stock forced out between taper die and head die.
毛刺:过多余量从锥模和顶模中挤出后引起的软滚子缺陷。
Almost all of these architecture structures are subjected to damage due to external loads, environmental effect, excessive service, natural disaster, initial design defect etc.
由于外部荷载、环境浸蚀、超期服役、自然灾害、设计初始缺陷等原因,这些建筑结构普遍存在损伤现象。
The results show that 82b wire rod brittle fracture is mainly caused by excessive inclusion, reticulate carbide, lower sorbite in the microstructure, and surface defect of wire rod.
结果表明,82 B钢盘条脆断的主要原因是夹杂物级别超标、组织中出现网状碳化物、索氏体含量偏低以及盘条表面缺陷等。