In contrast, the precursor can be transformed to pure-phase YAG when the calcining temperature is higher than 1100℃under the same conditions. The reason is that the propertied are different between alcohol-water solvent and distilled water solvent.
相反,在同样条件下水溶剂共沉淀所得前驱体需在高于1100℃的热处理温度下才能完全转变为纯相YAG粉体,其原因主要在于醇水溶剂性能与水溶剂性能不同。