The types of those cracks are summarized as three kinds: plastic shrinkage cracking, dry shrinkage cracking and hydration heat cracking.
将引起混凝土裂缝的类型归纳为塑性收缩开裂 ,干燥收缩开裂 ,水化热开裂三种 ,并对其表象及成因进行了阐述。
During the mass concrete construction in bridge structure, the cement hydration heat is easy to cause surface cracking.
大体积混凝土在桥梁施工过程中,由于水泥水化热容易引起表面裂缝。
The early cracking of concrete is usually caused by dry shrinkage, autogenous shrinkage of cement hydration and thermal-strain by hydration heat of cement.
混凝土的早期开裂主要是由于混凝土失水所产生的干燥收缩、水泥水化所产生的混凝土自收缩以及水泥水化热所产生的温度应变所引起。