The failure modes of the combination valve hot forging die in normal working condition are wear, collapse or cold hot fatigue crack.
气门锻模正常失效方式为磨损、压塌和冷热疲劳裂纹。
Through the pipe sample cutting and analyzing the crack in the fillet weld between the hot reheat pipe and the warming pipe, it was found out that the cause of the crack is due to the thermal fatigue.
通过对再热热段至低旁暖管管道角焊缝上裂纹的解剖分析,其原因是热疲劳裂纹引起的。