The corrosion weight loss rate and impact toughness of high Mn steel in hot concentrated caustic solution were studied by using immersed corrosion, impact test and SEM.
采用浸泡腐蚀试验和腐蚀前后的冲击试验并借助于扫描电镜观察,研究了热强碱介质中高锰钢的腐蚀速率和冲击韧度。
Under hot concentrated caustic impact-corrosion-abrasion conditions high Mn steel may be failure in earlier time.
在伴有冲击的热强碱腐蚀磨损工况,高锰钢有过早失效的危险。