An automatic compliance crack length measurement system for fatigue crack propagation test was used in the experiments.
研究中应用了一种柔度法疲劳裂纹自动测量系统进行裂纹长度测量。
On the basis of this, an automatic measurement technique of fatigue crack length in fatigue crack growth rate test under corrosive circumstance is established.
在此基础上,建立了腐蚀环境下疲劳裂纹扩展速率试验中裂纹长度的自动检测技术。
Plenty of oxidation etching pits are found on the surface of the specimen after the thermal fatigue test, and the surface principal crack is prone to propagate through these etching pits.
实验结果发现,试样表面出现大量的氧化腐蚀坑,表面主裂纹优先通过这些腐蚀坑扩展。