This paper gives a comprehensive failure analysis on the thermal fatigue crack of engine exhaust manifold and makes an improvement for materials and structures.
对某车型发动机排气歧管的热疲劳断裂问题进行综合失效分析,并从材料、结构方面提出改进意见。
Through the comprehensive analysis, the result shows that crack failure reason is embrittlement of the austenite stainless steel at high temperature.
通过综合分析指出对流管发生失效的原因是奥氏体不锈钢长期在高温下工作引起的热脆化开裂。
Some in-site vibrating test and metal fracture analysis have been done to reveal that the crack of the U-shaped bolts is fatigue failure and some reference for designer is put forward.
结合桥梁—人行道系统的现场振动测试和螺栓试样断口分析结果,指出既有桥上发生的U型螺栓破断属于疲劳破坏,并提出了改进意见。