low temperature sintering densification 低温烧结致密化
Densification and Sintering Process 致密化和烧结过程
sintering densification process 烧结致密化
sintering densification mechanism 烧结致密化机理
0.5wt% metal Cr could decrease obviously the oxygen partial pressure in the sample. Meanwhile, because the expansion caused by the oxidation reaction was small, Cr_2O_3 materials could realize the densification sintering at higher oxygen partial pressure (10-2atm and 10-4atm).
0.5wt%的金属Cr即可明显降低试样内部氧分压,且由于此时氧化反应引起的膨胀小,Cr_2O_3材料在10-2atm和10-4atm的较高氧分压下即可实现致密化烧结。
参考来源 - 添加剂对致密氧化铬材料烧结性能的影响·2,447,543篇论文数据，部分数据来源于NoteExpress