钢铁以及有色金属中出现延迟断裂（Delayed Fracture）、应力腐蚀开裂（Stress Corrosion Cracking）都侧面地反映了氢脆的作用和影响。
基于76个网页-相关网页
hydrogen-induced delayed fracture 氢致滞后断裂 ; 氢诱发延迟性碎裂
hydrogen induced delayed fracture 氢致延迟断裂
electric field-induced delayed fracture 电致滞后断裂
delayed-fracture time 延迟断裂时间
anti-delayed fracture 耐延迟断裂
delayed fracture union 骨折延迟连接
delayed fracture healing 骨折延迟愈合
delayed fracture behavior 延迟断裂行为
delayed fracture property 延迟断裂性能
Delayed fracture resistance of the tested steels increases with the increase of boron content, which are also higher than that of conventional steel 60Si2Mn at same strength level.
实验钢的延迟断裂抗力随着钢中硼含量的增加而逐渐增加，且高于传统的弹簧钢60Si2Mn。
参考来源 - 硼对高强度弹簧钢组织与性能的影响·2,447,543篇论文数据，部分数据来源于NoteExpress
Fastener common failure mode of failure of the assembly has elongated, fatigue fracture and delayed fracture.
紧固件失效的常见失效形式有装配拉长、疲劳断裂和延迟断裂。
The role of atomic hydrogen and hydrogen-induced martensite in hydrogen-induced delayed fracture was very small.
而原子氢和氢致马氏体在氢致滞后断裂中所起的作用则极小。
It was observed that the delayed fracture resistance of 30MnSi steel bars increases with tempering temperature at a sufficient strength.
在保证强度满足要求的前提下提高回火温度可以提高钢的耐延迟断裂性能。