The results indicated the sample of the cubic phase ZrO2 stabilization,density and conductivity increased by doping Y. The phase was cubic phase ZrO2,the density reached 5.48g/cm3 and conductivity reached 2.85×10-3S·cm-1 at 700℃,when the sample contained Y as 20mol%.
当Y元素掺量为20mol%时,试样的物相为立方相ZrO2,试样的密度达5.48g/cm3,其在700℃的电导率为2.85×10-3S.cm-1。
参考来源 - 氧化锆基复合电解质材料研究·2,447,543篇论文数据，部分数据来源于NoteExpress
We also study the relation between the dielectric constant and lattice distortion of the PT tetragonal and cubic phase region.
我们还研究了PT四方相区和立方相区介电常数与晶格畸变的关系。
The formation of cubic phase in zirconia stabilized with Y_2O_3is discussed.
本文从结构化学的角度讨论了掺y_2o_3后氧化锆形成立方相的原因。
The results indicate that the coating is mainly composed of tetragonal and cubic phase and a small amount of monoclinic zirconia.
结果表明，涂层主要以四方相和立方相构成，并含有少量的单斜相。