Through the dry and wet cycling experiment on concrete members, RMA's influence on corrosion of steel bars are studied,and the position of initial corrosion and the corrosion amount of the reinforcing bar are analyzed in different RMA's content.
通过干湿循环试验研究了耐蚀剂对钢筋锈蚀的影响，分析了不同保护层厚度、不同耐蚀剂含量对钢筋锈蚀开始时间及锈蚀程度的影响。
参考来源 - 海洋环境下混凝土结构耐久性研究·2,447,543篇论文数据，部分数据来源于NoteExpress
Corrosion of steel bars in concrete port structures is a serous problem throughout the world.
钢筋锈蚀引起混凝土码头结构的过早破坏，已经成为全世界普遍关注并日益突出的问题。
This paper analyses the mechanism of corrosion of steel bars, interprets the theory of concrete structure crack control and poses measures of narrowing the cracks.
分析了混凝土结构的受力钢筋腐蚀机理，阐述了钢筋混凝土结构的裂缝控制理论，以及减小钢筋混凝土结构裂缝宽度的措施。
The rust experiment on steel bars embedded in mortar shows the environmental temperature has great influence on the rust corrosion rate of steel bars.
根据对砂浆中埋置钢筋的试件进行室内快速锈蚀试验研究的结果，环境温度对钢筋锈蚀率有重要的影响。