The effective methods to avoid the cracking include lowering strictly the content of impurity and adopting low temperature welding process.
有效的改进措施是严格控制杂质含量、将高温焊接工艺改为低温焊接工艺。
The results show that high content of impurity elements, segregation along grain boundaries and uneven grain size are main reasons for the surface damage of domestic tung...
结果显示，杂质元素的含量偏高和沿晶界的偏析以及不均匀的钨晶粒是造成国产钨靶表面损伤的主要原因。
The results show that high content of impurity elements, segregation along grain boundaries and uneven grain size are main reasons for the surface damage of domestic tungsten targets.
结果显示，杂质元素的含量偏高和沿晶界的偏析以及不均匀的钨晶粒是造成国产钨靶表面损伤的主要原因。