The chemical stress cracking of PET fiber-methylamine system is considered to be a fracture phenomenon of polymers.
PET纤维-甲胺系统的化学应力开裂被归结为一种高聚物断裂破坏现象。
Delamination and cause of polycarbonate (PC) thin-wall component were studied by comprehensive analysis methods and chemical stress cracking mechanism of PC delamination was found.
应用综合分析方法研究了聚碳酸酯(PC)薄壁件分层开裂及其起因，发现了分层的化学应力开裂机制。
Authors inter-prete all experimental results of the work with the molecular mechanism of fracture behaviour of polymers and propose the mechanism of chemical stress cracking of PET-methylamine system.
作者从高聚物断裂的微观机理解释了所有实验结果并提出PET -甲胺系统化学应力开裂机理。