Neutron irradiation-induced phosphorus intergranular segregation in the reactor pressure vessel steels is the one of main reasons resulting in brittle fracture of the nuclear reactor vessel.
中子辐照引起的核反应堆压力容器钢中磷的晶间偏析是导致核反应堆压力容器脆性断裂的主要因素之一。
The fracture of the material was diverted from the manner of intergranular brittle fracture to the manner of intergranular brittle fracture with dimple gliding fracture.
材料的断裂方式由沿晶脆性断裂转变为沿晶脆性断裂和韧窝韧性断裂的混合断裂方式。
High manganese steels undergo a ductile to brittle transition at low temperature, which is accompanied by a change in the fracture mechanism from dimple fracture to intergranular fracture.
高锰奥氏体钢随温度降低其断裂机制由韧窝状断裂转变到晶界断裂。