  In short,according to lots of experiments,the best paste was containing 30%～35%F resin and 65%～70% silver-coated glass bead ,then the paste was cured at 140℃ for about 30 min.

  综上所述，通过大量的实验研究发现，最佳性能的浆料是用F树脂30％～35％加入65％～70％的银包玻璃微珠粉调制浆料，然后在140℃下保温固化30min。