蒙乃尔400目 免疫氯离子应力腐蚀开裂在典型环境。
Monel 400 mesh is immune to chloride ion stress corrosion cracking in typical environments.
结果表明，不锈钢盘管失效的原因是氯离子引起的应力腐蚀开裂所致。
The result indicated that the failure cause of the stainless steel spiral pipe is the stress corrosion crack induced by Cl- ion.
结果表明，介质中所含的微量氯离子引起的晶间型应力腐蚀开裂导致再沸器失效。
The result showed that the direct reason of reboiler invalidation was the intercrystalline stress corrosion and crack caused by micro-chloride in the medium.