Chloride stress corrosion cracking(CLSCC) 氯化物应力腐蚀开裂 Corrosion Under Insulation 保温层下腐蚀 ..
基于24个网页-相关网页
氯化物应力腐蚀开裂
Chloride stress corrosion cracking
以上为机器翻译结果，长、整句建议使用 人工翻译 。
失效原因是由于在其管外壁的局部环境中氯化物的富集而发生点蚀，进而引发管子应力腐蚀开裂，最终造成管内氢气的泄漏。
Results show that the material is 316 stainless steel, and the failure was due to pitting induced by chloride which was enriched from the enviroment in the medium in local areas of it…