腐蚀试样的表面状态（粗糙程度）对母材金属的耐点蚀性能有明显的影响。
The surface condition (roughness) of corrosion test sample has a pronounced influence on the pitting resistance of the base metal.
碳扩散的结果是在紧邻熔合界面的焊缝金属一侧形成高硬度的增碳层，母材金属一侧产生硬度较低的贫碳层。
Carbon migration induces the formation of carbon-enriched layer in the austenitic weld metal and carbon-denuded layer in the Cr-Mo steels base metals.
焊接接头的拉伸试验断裂部位在焊缝。焊接HAZ熔合线附近的硬度值最高，远离熔合线硬度降低，并逐渐接近母材金属的硬度。
The tensile test fracture area locates on weld seam, and the hardness near HAZ fusion line is the highest, away from the fusion line, the hardness declines and reach the parent metal hardness.