残留奥氏体(retained austenite) 残留奥氏体:工件淬火时由于马氏体转变时发生体积膨胀,马氏体转变结束时总有少量奥氏体被保留下来,冷却至室温后残存的奥氏体。
...残留奥氏体形成的关系 关键词 :RIP钢;残留奥氏体;临界区退火;等温淬火 [gap=895]Key words: TRIP steel; retained austenite; intercritical annealing; austempering ...
基于582个网页-相关网页
... residual strain 剩余应变,残余应变... residual austenite 残留奥氏体 residual oil 残余油,残油...
基于10个网页-相关网页
After 1050℃quenching temperature was treated,cryptocrystalline martensite,the retained carbides,and the retained austenite are observed in these bearing steel's microstructure.
淬火温度在1050℃热处理条件下,4种不锈轴承钢基体为隐晶马氏体+未溶碳化物+残留奥氏体。
参考来源 - 碳、铬含量对不锈轴承钢组织和接触疲劳性能的影响·2,447,543篇论文数据,部分数据来源于NoteExpress
用X射线衍射法对表层残留奥氏体和残余应力作了定量分析。
The residual compressive stress and retained austenite were analyzed quantitatively by XRay Diffraction.
还探讨了合金元素对等温转变过程中残留奥氏体量的影响规律。
The affecting rule of alloy elements on the amounts of retained austenite in austempering transformation was also studied.
结果表明,热轧后能够获得多边形铁素体、粒状贝氏体和大量稳定的残留奥氏体组织。
The results show that polygonal ferrite, granular bainite and larger amount of stabilized retained austenite can be obtained after hot rolling.