循环续循环模拟计算出裂纹从初始长度一直到疲劳破坏的扩展曲线。
The fatigue crack growth curve from initial crack size till fatigue failure is simulated step by step.
裂纹扩展曲线的建模是基于概率断裂力学的耐久性分析方法的前提。
Modeling of crack growth curve is the premise of the durability analysis based on probabilistic fracture mechanism.
完成了连铸和模铸LZ50车轴钢疲劳裂纹扩展试验,得到了两类LZ50车轴钢的疲劳裂纹扩展曲线。
The fatigue crack propagation testing were completed for CT specimens of LZ50 axle steels with continuous casting and mould casting.