...对像,采用原子断层分析技术(APT),X射线光电子能谱(XPS),极化曲线,交流阻抗谱,Mott-Schottky,FeCl3浸泡并结合慢应变速率拉伸(SSRT),研究了不同时效制度下高强度不锈钢微观结构的演变规律及其对腐蚀的影响,得到以下主要结论:15-5PH钢时效早期Cu原子从基体脱溶形成...
基于132个网页-相关网页
...术信息平台 关键词： 铝镁合金；慢应变速率拉伸；应力腐蚀敏感性 [gap=985]Key words: Al–Mg alloys; slow strain rate tension; stress corrosion cracking susceptibility ...
基于18个网页-相关网页
用光滑试样慢应变速率拉伸法研究了X60管线钢在含水土壤中的应力腐蚀。
Stress corrosion cracking of an X60 pipeline steel in soil containing water has been investigated using slow strain rate test.
用慢应变速率拉伸(SSRT)技术研究了7075铝合金在应力腐蚀过程中的力学与电化学交互作用。
The interaction between mechanics and electrochemistry during the stress corrosion cracking (SCC) of 7075 aluminum alloy was studied using slow strain rate tension (SSRT) technique.
采用恒载荷和慢应变速率动态拉伸实验方法，测定了X80管道钢在不同充氢条件下的氢致开裂门槛应力和断裂应力。
The threshold stress and fracture stress of hydrogen-induced cracking of X80 pipeline steel are studied by constant load test and slow stain rate test.