When tempering temperature further heightens, he hardness descends gradually.
当回火温度进一步升高时,硬度逐渐降低。
参考来源 - 热处理工艺对Cr13型不锈钢组织和性能的影响When the temper temperature rose to 720 掳C ,the carbide get aggregated.
回火温度升至720℃时,碳化物粒子有聚集长大的趋势。
参考来源 - 23MnNiCrMo54圆环链用钢组织及性能研究·2,447,543篇论文数据,部分数据来源于NoteExpress
当回火温度进一步升高时,硬度逐渐降低。
When tempering temperature further heightens, he hardness descends gradually.
建立了回火硬度与回火温度关系的回火效应模型。
The tempering behavior model of relationship between tempering hardness and temperature was set up.
MIM钢试样的疲劳强度随着回火温度升高而减低。
Fatigue strength of the MIM specimens declined with increasing tempering temperature.