退火后,孪晶逐渐消失,形成等轴的再结晶晶粒。
The twins disappeared gradually and recrystallized grains formed after annealing.
退火后,孪晶逐渐消失,形成等轴的再结晶晶粒。
The twinning disappeared gradually and recrystallized grains formed after annealing.
指出,孪晶位错是再结晶过程中,孪晶界面迁移的激活台阶。
It is showed that twin dislocation is the activated step of the migration of twin-plane boundary during recrystallization.