轴承零件在淬火冷却过程中因内应力所形成的裂纹称淬火裂纹。
Bearing parts in the process of hardening cooling by internal stress due to the formation of quenching cracks crack said.
从宽带钢板形、内应力、冷弯裂纹及板带表面缺陷等几个方面进行了分析，并提出了相应的对策和解决办法。
The profile, internal stress, cold - bending cracks and surface flaws of the hot strip have been analyzed, and the corresponding strategics and resolutions are also preferred, In order to improve the.
总之，造成淬火裂纹的原因可能是上述因素的一种或多种，内应力的存在是形成淬火裂纹的主要原因。
In short, the causes of cracks caused by hardening of these factors may be one or more, the existence of internal stress is the main reason for the formation of quenching cracks.