The experimental results show that the swelling quantity and characteristics of the blended membrane are related to the dose of crosslinking agent and blend ratio.
实验结果表明，膜的溶胀量及分离性能与共聚物的交联剂用量及膜的共混比有关。
Their tensile strength and elongation at break were obviously dependent on irradiation dose and blending ratio of the polymers.
该膜的抗张强度和断裂伸长率则明显地依赖于辐射剂量和聚合物的混合比例。
The effect of resin compounding ratio and radiation dose on blends of epoxy resin 828 and 648 systems was analyzed.
分析了树脂配比及辐射剂量对环氧828／648树脂混合体系的影响；