After heat treatment, the degree of graphitization of the materials was about 30~50%, and the degree of graphitization of material l-6
石墨化热处理后，材料石墨化度约30～50％，其中1-6材料的石墨化度达到47.1％。
参考来源 - 航空发动机轴间密封C/C复合材料的制备及摩擦磨损特性研究High degree of graphitization in this manganese oxides coated fibers is observed clearly at HTT of 1600℃.
在1600℃下热处理就能得到高石墨化度炭纤维。
参考来源 - 聚丙烯腈基炭纤维的催化石墨化研究·2,447,543篇论文数据，部分数据来源于NoteExpress
The results indicate that the content of carbon is about 90%, the degree of graphitization is 66% and the carbon of simple substance phase at the surface is 54%.
结果表明纳米石墨中碳含量为90%左右，石墨化度为66%，表面碳原子以碳单质状态存在的占54%。
The experimental results showed that the effect of the purity, degree of graphitization, microstructure etc. factors on the synthesis result of diamond and properties.
由实验结果可以看出、石墨材料的纯度、 石墨化度、显微组织结构等因素，对金刚石的合成效果及其性能均有显著的影响。
The results show that the higher graphitization degree of pitch derived carbon is, the higher real density is.
沥青炭的室温电阻率随石墨化度的增加而下降，随体积密度的增大而下降；