... 连续冷却转变全迅网(CCT全迅网) continuous cooling transformation 裂纹敏感性 cracking sensibility 焊接裂纹 weld crack ...
基于78个网页-相关网页
On the base of orthogonal comparison tests, influences of many kinds of factors on the cracking sensibility of plasma clad coatings have been studied in this paper.
本文采用正交对比试验,研究了多种因素对等离子熔覆铁基涂层开裂敏感性的影响。
The cold cracking sensibility of high tensile pipeline-steel was studied by Ygroove cracking test using seven kinds of high cellulose electrode of vertical down position welding.
采用七种高纤维素型立向下电焊条,通过斜y坡口裂纹实验,对高强管线钢的冷裂敏感性进行实验研究。
The increase of weld current can reduce the hardness and the content of upper bainite, and lower the sensibility of hydrogen cracking of the joints.
在避免烧穿的前提下增大焊接电流能够减小硬度、减少上贝氏体,从而降低氢致开裂敏感性。