Furthermore, the corrosion weight loss experiment confirms that the coating witnesses the low loss rate and well anti-corrosion.
在腐蚀失重实验中,失重率低,耐蚀性能好。
参考来源 - 钢丝圈表面耐磨耐蚀涂层的理论与试验研究·2,447,543篇论文数据,部分数据来源于NoteExpress
The results showed that the corrosion weight loss rate of high Mn steel was distinctly greater than that of medium carbon chromium steel.
结果表明,高锰钢的平均腐蚀速率显著高于中碳铬合金钢,腐蚀过程中高锰钢有较严重的碱脆开裂现象。
The corrosion weight loss rate and impact toughness of high Mn steel in hot concentrated caustic solution were studied by using immersed corrosion, impact test and SEM.
采用浸泡腐蚀试验和腐蚀前后的冲击试验并借助于扫描电镜观察,研究了热强碱介质中高锰钢的腐蚀速率和冲击韧度。
Salt concentration difference macrocell corrosion of X70 steel in yellow pebble soil was studied by means of EIS and weight loss method.
利用电化学阻抗法和失重法,研究了X70钢在卵石黄泥土中的盐浓差宏电池腐蚀。