The existing cooling ability of bloom continuous casting mold at PZH Steel was evaluated, then, the mold cooling process was optimized.
在分析攀钢大方坯连铸现行结晶器冷却能力的基础上,优化调整了结晶器冷却制度。
After all, the choice and control of continuous casting process parameters are also different during continuous casting different steel grade.
由此,在连铸不同钢种时,连铸工艺参数的选择与控制的重点也各不相同。
The smelting parameters and continuous-casting process in developing carbon welding rod steel of H08A are introduced, the cause for success and lost is analyzed, some measures proposed.
介绍了宣钢试验碳素焊条钢h 08 A的冶炼参数和连铸工艺,分析了试验成功的原因和失败的教训,提出了解决措施。