The results from the effect of compatilizer on rheological behavior of composites indicated that torque balanced augments linearly with the increase of compatilizer content. However,it did not cause much difficulty for the melt processing.
相容剂用量的增加导致了平衡扭矩线性的提高,但对实际加工并没有带来太大的影响。
参考来源 - 相容剂对长玻纤增强尼龙66树脂力学性能和流变行为的影响The results indicated that the compatilizer enhanced the impact strength and breaking elongation of PC/ABS alloy obviously, enhanced all mechanical properties of PA6/ABS alloy, and enhanced the tensile strength and breaking elongation of ABS/GF composite.
结果表明,该增容剂的加入明显提高了PC/ABS合金的冲击强度和断裂伸长率,使PA6/ABS合金的各项力学性能均明显提高,使ABS/GF复合材料的拉伸强度和断裂伸长率也有较大提高。
参考来源 - 马来酸酐接枝ABS的增容改性研究When the content of compatilizer were 15wt%~30wt%(to high density polyethylene), the intercalation high density polyethylene /bentonite nanocomposites were obtained.
当相容剂含量为15wt%~30wt%(对于高密度聚乙烯),能够得到插层型高密度聚乙烯/膨润土纳米复合材料。
参考来源 - 熔融插层法制备聚乙烯/膨润土纳米复合材料的研究·2,447,543篇论文数据,部分数据来源于NoteExpress
The effect of compatilizer and toughener on the properties of modified PA6 /PA66 is studied.
研究了相容剂、增韧剂对改性尼龙6/尼龙66合金性能的影响。
The effects of grafting ratio on mechanical property of the system are studied by adding the produced compatilizer to the LDPE/MH system.
通过制备的接枝物添加到阻燃体系中,考察了接枝率对体系性能的影响。
By adopting various types of compatilizer, this paper has studied and developed Starch plastics. With good mechanical properties as well as suitable degradable properties.
采用多种增容剂.研究与制备淀粉基塑料.使之既有良好的力学性能、又有较好的降解性能。