welding cold crack 焊接冷裂纹
welding cold crack sensibility 焊接冷裂纹敏感性
Welding Cold Crack Sensitivity 焊接冷裂纹敏感性
low welding cold crack sensitivity 低焊接裂纹敏感性
And analyzes the reason and forming mechanism of the defects such as cold crack, air porosity and oxidation etc. proposes the measures of welding process to ensure the welding quality.
分析钛材管道焊接产生的冷裂纹、气孔、氧化等缺陷的原因和形成机理，提出焊接工艺措施，以确保焊接的质量。
The results show that using HTG-1 electrode may effectively decrease welding cold crack sensitivity of the steel, and the sensitivity to cold crack decreases as preheating temperature increases.
结果表明：采用HTG - 1焊条可以有效地降低该钢焊接冷裂纹敏感性；预热温度增加，抗冷裂效果更好。
During the manufacture of oil derrick, such factors as welding defects, deforming and cold crack have key effect on the oil derrick quality.
在井架的制造过程中，焊接缺陷、焊接变形和焊接冷裂纹是影响井架质量的关键因素。