铸造缺陷 - 引用次数：11
But with the rapid development applicationof the technology, casting defect was emerged especially in large castings, andsometimes resulted in reject.
但是，随着电渣熔铸技术的不断推广应用，尤其在生产大型铸件时，也会出现内部铸造缺陷，最终导致铸件报废。
参考来源 - 电渣熔铸大型水轮机导叶内部缺陷研究 -
铸造缺陷 - 引用次数：2
In casting defect recognition of an X-Ray image,due to the complex image background,it is difficult to do segmentation with traditional segmentation technology for interested regions,in which the defects are intense.
在利用X射线对铸造缺陷识别的过程中,由于X光图像中铸件形成的背景复杂,传统的区域分割技术难以分割出缺陷集中的兴趣区域。
参考来源 - 一种在铸件缺陷识别中的区域分形分割方法 in C -
铸疵铸件缺陷铸物缺陷铸造缺陷
-
铸疵
·2,447,543篇论文数据，部分数据来源于NoteExpress
Casting defect
- abstract: A casting defect is an irregularity in the metal casting process that is undesired. Some defects can be tolerated while others can be repaired otherwise they must be eliminated.
以上来源于: WordNet
双语例句
-
Numerical simulation for casting process may optimize craft design, shorting trial cycle, cut the cost, decrease casting defect and assure the casting quality.
铸造过程的数值模拟可以优化工艺设计，缩短产品试制周期，降低成本，减少铸件缺陷，确保铸件质量。
-
The results showed that the root reason for valve body failure was seriously casting defect exist and its big and density shrinkage porosity form the original crack;
结果得出：阀体失效的主要原因是阀体本身存在严重的铸造缺陷，铸造疏松严重、孔洞尺寸大乃于形成原始裂纹源；
-
The results show that the partial unmelted region, casting defect structure and secondary crack form in the welding seam, which result in the low stress breakage of the samples.
结果表明：在焊缝区域内存在着局部未熔区以及铸造疏松组织和二次裂纹等缺陷，这是导致试样低应力断裂的根本原因。