The maximum tensile strength is 329.5MPa, increased 104% comparing with as cast condition, the maximum elongation percentage could reach 2.2%.
最大抗拉强度达到了329.5MPa,比铸态提高了104%;最大伸长率达到了2.2%。
参考来源 - 半固态成形Al·2,447,543篇论文数据，部分数据来源于NoteExpress
The damping capacity in cast condition is dependent on strain amplitude, and it increases with its enhancement.
铸态合金的阻尼性能与应变振幅有关，随着应变振幅的提高而不断提高；
The as-cast bainite steel studied in this paper could obtain bainite directly in the as-cast condition through alloying and controlling the cast cooling rate without heat treatment.
所研究的铸态贝氏体钢是通过合金化和控制冷却速度的方法在铸态下直接得到贝氏体组织的，不需热处理即可获得所需的组织和性能。
A new production process was developed through finite element simulation. The microstructure and mechanical properties of grates at both heat treatment and as-cast condition were analyzed.
通过有限元模拟改进了原炉排制造工艺，对新工艺制造的炉排件进行取样并分析了铸态和热处理前后的显微组织和力学性能。