And the bone china body with good fluidity,high whiteness and high bending strength could be obtained when the average-median-size of bone ash,kaolin,feldspar and quartz were about 0.90μm、4.39μm、2.40μm、8.04μm respectively.4.
实验表明,当骨粉、高岭土、长石、石英的平均中值粒径D50分别为0.90μm、4.39μm、2.40μm、8.04μm左右时,可制备流动性好,白度和抗弯强度高的骨质瓷坯体。
参考来源 - 新型骨质瓷制备工艺与性能研究·2,447,543篇论文数据，部分数据来源于NoteExpress
以上来源于: WordNet
N the residue obtained when bones are burned in air, consisting mainly of calcium phosphate. It is used as a fertilizer and in the manufacture of bone china 骨灰
At last the weight of bone ash and calcium content were measured.
最后进行灰重及骨钙含量的测定。
Bone China porcelain is basically made by adding bone ash to kaolin and petuntse.
骨瓷的基本成分是加入骨粉的高岭土和白墩子。
Small porous bowl made of bone ash used in assaying to separate precious metals from e. g. lead.
用来分析试验以从铅中分离贵重金属的用骨灰制成的小的多孔渗水的碗。