Bonding force of substrate and adhesive layer is large. No adhesive failure occurs during storage and construction.
基材与胶层结合力大，在存放或施工过程中不存在脱胶现象。
The fracture modes observed by using multiplication microscope indicated that the adhesive failure was the most mode of fracture.
断裂方式观察结果显示绝大部分样本的断裂方式都是粘结面型断裂。
The reason of the failure of epoxy bonded joint in water was that the epoxy adhesive on the metal surface was substituted for water.
环氧胶接接头在水中破坏失效的原因主要是渗入到胶接层的水分子取代了胶粘剂分子在金属表面的粘附。