与经普通淬火和高温回火的相比，经磁场淬火和高温回火的T10钢的抗拉强度提高了28%，断后伸长率提高了8。
The tensile strength, elongation and hardness of T10 steel subjected to magnetic field quenching and to high temperature tempering were separately increased by 28%, by 8.
本文研究了不同热处理时效温度和时效时间对一种活塞环用钴基高温合金的抗拉强度、延伸率、硬度及组织的影响。
The effect of aging treatment on the tensile strength, elongation, hardness and microstructure of a cobalt base superalloy used for pistons rings was investigated in this paper.
随着铁含量增加，合金的高温短时抗拉强度增加，但室温抗拉强度下降。
It is demonstrated that the high temperature temporal strength increases with the increasing of iron content while as the room temperature strength decreases.