与经普通淬火和高温回火的相比，经磁场淬火和高温回火的T10钢的抗拉强度提高了28%，断后伸长率提高了8。
The tensile strength, elongation and hardness of T10 steel subjected to magnetic field quenching and to high temperature tempering were separately increased by 28%, by 8.
含氮奥氏体不锈钢的安全角优于硬度为HRC33.7和HRC30.1的高温回火中碳钢，前者具有较高的抗弹丸倾斜入射的能力。
The safe Angle of nitrogen alloyed austenitic stainless steel is better than high tempered middle carbon steel of HRC33.7 and HRC30.1 in hardness.
通过高温抗氧化、盐雾腐蚀和应力腐蚀试验研究了07X16H6沉淀硬化不锈钢在使用状态（回火态）时的耐蚀性能。
The corrosion resistance of 07X16H6 precipitation hardening stainless steel in tempered state was studied using high temperature oxidation, salt-spray test and stress corrosion test.