基于各向同性弹塑性损伤假定和应变等效假设，采用重复拉伸的试验方法，得到了焊缝金属的损伤演化规律。
Based on the adoption of elastoplastic damage theory and effective strain assumption, weld metal coupons were tested under repeated pull and their damage evolution law was determined.
通过对钢筋与金属套筒之间采用植筋胶粘结的拉伸抗剪试验，探讨了植筋胶的粘结机理和拉伸抗剪破坏模式。
Through pullout tests for shear resistance of the adhesive steel bar in the metal tube, the bond principals and failure modes of adhesives are studied.
焊接接头的拉伸试验断裂部位在焊缝。焊接HAZ熔合线附近的硬度值最高，远离熔合线硬度降低，并逐渐接近母材金属的硬度。
The tensile test fracture area locates on weld seam, and the hardness near HAZ fusion line is the highest, away from the fusion line, the hardness declines and reach the parent metal hardness.