结果表明,电位振荡现象是由于蚀孔内形成盐膜所引起的。
Experimental results showed that the electrochemical oscillation was caused by the salt film formed within pits.
钛合金ta7在盐酸-甲醇溶液中的应力腐蚀裂纹源自点蚀孔底部。
It shows that the SCC susceptibility occurs in methanol solution. SCC of TA7 originates from the...
海船压载舱使用海水压载,引起船体板的腐蚀,焊缝处会产生蚀孔漏水。
The use of sea water in ballast water tank of sea-going ships causes the corrosion of ship hull plates and the water leak from the corroded holes at welding seams.