而在高温低周疲劳条件下裂纹是在粘结层与高温合金基体的扩散层处。
However, cracks initialized in the diffusion layer between substrate and bond coat when TBCs were tested with low cycle fatigue at high temperature.
而在高温或高浓度的碱性溶液中薄膜表面难以形成稳定的钝化保护层。
Nevertheless, in higher temperature or solution concentration of the alkaline solutions, the formation of stable passive layer is very difficulty.
而在高温辐照条件下，即使辐照剂量率较高，其辐射损伤也有显著的差异。
However, while irradiated at elevated temperatures, even the irradiation dose-rate is higher, the radiation damage of the transistor has marked difference.