在对各项试验结果进行综合分析之后确认，该管路泄漏失效为应力腐蚀破坏。
After the integrated analysis of each test result, it is proved that the pipe leakage failure is of stress corrosion damage.
管路所用材料的材质状况(化学成分、显微组织等)不佳，是造成应力腐蚀破坏的主要因素。
The low quality of pipe material (chemical component, microstructure) is the main reason to result in stress corrosion damage.