解决这一问题的关键是扩大铸坯等轴晶区比例,细化晶粒。
The key to solve these problems is enlarging equiaxed grain zone and fining grain size.
退火后,孪晶逐渐消失,形成等轴的再结晶晶粒。
The twins disappeared gradually and recrystallized grains formed after annealing.
退火后,孪晶逐渐消失,形成等轴的再结晶晶粒。
The twinning disappeared gradually and recrystallized grains formed after annealing.