过滤后铸棒组织中的柱状晶区缩小，中心等轴晶区扩大、晶粒度降低。
The area of columnar structures decreased, and that of equiaxed crystals enlarged. The grain size reduced.
解决这一问题的关键是扩大铸坯等轴晶区比例，细化晶粒。
The key to solve these problems is enlarging equiaxed grain zone and fining grain size.
结果表明，激光处理后试样表面熔凝区的组织主要为胞状枝晶组织，经后续热处理可转变为细小的等轴晶粒组织，并形成了良好的超塑连接条件。
The results show that, after laser surface processing, a melt layer with cellular-dendrite structure is formed, which could transform into very fine-grained structure during the annealing treatment.