其中第一、二节热器管内主要为溶解氧腐蚀，而盘管内主要为高温蒸汽的冲刷+腐蚀。
The heating tubes in the 1st section mainly suffer from corrosion of dissolved oxygen while those in the 2nd section suffer from erosion corrosion of high-temperature steam.
特别在溶解氧浓度有差别的场合，浓差电池常引起严重腐蚀、导致孔蚀。
Severe corrosion, leading to pitting, is often caused by concentration cells, particularly where differences in dissolved-oxygen concentration occur.
针对水箱中高湿热腐蚀环境，介绍了涂层在热水、 溶解氧及腐蚀性氯离子等影响因素作用下发生的鼓泡、脱落、湿附着力丧失等现象。
The bubbling, flaking, loss of wet adhesion and et al of the coating film occurred under the action of hot water, dissolved oxygen, corrosive chlorium and et al are introduced.